X-ray CT dataset of a secondary Li-ion Battery
Mitwirkende
Hosting institution:
Beschreibung
X-ray CT scan of a secondary Li-ion Battery by Eduardo Machado, Technical University of Graz. The goal was to observe the impact of mechanical deformation on the layers. Specimen scanned during a laboratory training on March 30, 2002. Isotropic voxel size = 15.5 µm. Please acknowledge Graz micro-computed Tomography Consortium and Eduardo Machado when using this data.
Technical info (English)
Scan Parameters:
- Scanner name =TESCAN UnitomXL; 180 kv reflection source; TU_Graz
- kV = 175
- Target current actual value = 171.7 µA
- Target power = 30
- Filter = Cu 1.5 mm
- Exposure = 280 ms
- Projections = 1440
- Average = 8
- Voxel size = 15.5 µm.
- SOD = 57.000076 mm
- SDD = 1100.000244 mm
- Scan type = smooth take and save
- Binning value = 2
- Unbinned pixelsize (mm) = 0.15
- Binned pixelsize (mm) = 0.3
Technical info (English)
Reconstruction Parameters (see #.rec.1.xml in directory):
- beam hardening correction = 0
- Scatter Correction = 0.01
- Noise attenuation filter = SheppLogan
- Noise attenuation value = 0.5
Dateien
00048XL_LiBattery.zip
Dateien
(1.1 GB)
Name | Größe | Download all |
---|---|---|
md5:1b9708b590e450cb8e126632db83237d
|
1.1 GB | Vorschau Herunterladen |
md5:fd2d38114c4a54faf90ac5ac59a20832
|
743.4 kB | Vorschau Herunterladen |
md5:cc2872b02e14ed69de83dfc1c8a1e1ac
|
377.1 kB | Vorschau Herunterladen |
Weitere Details
Daten
- Available
-
2022-11-21